ZIRCONIO ST WHITE
Santa Barbara SRL
Zirconia material for dental applications with high purity composition (≥99% ZrO2+HfO2+Y2O3). Available in various disc sizes for sintering and milling applications.
Product Information
| Manufacturer | Santa Barbara SRL |
|---|---|
| Weight | 350 g |
| Composition | ZrO2+HfO2+Y2O3 ≥99% |
| Cytotoxicity | Level 0 |
| Other Oxides | <0.15% |
| Y2o3 Content | 4.5%-6.0% |
| Al2o3 Content | <0.15% |
| Cte 25 500°c | 10.5 ±0.05 |
| Radioactivity | <0.1 Bq·g−1 |
| Flexural strength | 1200 MPa |
| Chemical Solubility | <100 µg·cm−2 |
| Light Transmittance | 43% |
| Available Disc Sizes | ∅98×10, ∅98×12, ∅98×14, ∅98×16, ∅98×18, ∅98×20, ∅98×22, ∅98×25 mm |
| Sintering Temperature | 1500-1550°C (recommended 1530°C) |
| Density After Sintering | 6.09 ±0.01 g·cm−3 |
| Density Before Sintering | 3.15 ±0.05 g·cm−3 |
| Aging Surface Monoclinic Phase | <15% |