BAOT Universal Glaze Paste for Zirconia Porcelain and Multiple Dental Materials
Baot Biological Technology Co.,Ltd. · source
BAOT Universal Glaze Paste for Zirconia Porcelain and Multiple Dental Materials
BAOT Universal Glaze Paste is suitable for zirconia, PFM & PFZ and glass ceramic restorations. It provides natural gloss, stable shade and a smooth surface after firing. Easy to use and reliable, it helps dental technicians achieve high-quality aesthetic restorations.
Product Features
BAOT Universal Glaze Paste is a versatile glazing material designed for zirconia, PFM, PFZ and glass ceramic restorations. It provides a smooth surface, natural gloss and stable shade after firing. With its easy application and reliable performance, it helps dental technicians efficiently achieve aesthetic and consistent results in daily laboratory workflows.
Why Choose BAOT Universal Glaze?
Universal compatibility Suitable for zirconia, PFM, PFZ and glass ceramic restorations.
Natural gloss effect Creates a smooth surface and lifelike luster in just one firing.
Stable color performance Maintains consistent shade before and after firing.
Easy handling Smooth paste consistency allows convenient and precise application.
Efficient workflow Helps technicians complete glazing procedures quickly and reliably.
Product Specifications
Product Name BAOT Universal Glaze Paste
Type With fluorescence / Non-fluorescent
Net Weight 5g / jar
Firing Temperature 730–950 °C
Compatible Materials Zirconia, PFM, PFZ, and Glass Ceramic
Indications Glazing for crowns, bridges and veneers
Application Method Brush application before firing
Surface Effect Natural gloss and smooth surface after firing
Physical Data
| Standard | Specification | Values |
|---|---|---|
| Coefficient of thermal expansion (25-475℃)[·10⁻⁶·K⁻¹ ±0.5] | EN ISO 6872 | 9.5 |
| Transformation temperature Tg [°C ±20] | EN ISO 6872 | 495 |
| Bending strength [MPa] | EN ISO 6872 | ≥50 |
| Solubility [μg/cm2] | EN ISO 6872 | ＜100 |
Firing Chart
| Start Temperature [℃] | Drying Time [min] | Heating Time [min] | Heating Rate [℃/min] | Final Temperature [℃] | Holding Time [min] | Cooling Time [min] | Cooling Temperature [℃] |
|---|---|---|---|---|---|---|---|
| 400 | 3 | 4 | 45 | 730-950 | 1 | 4 | 400 |
Firing Instructions
Please note before firing:
If needed, Stain Structure Gingiva and Glaze can be fired together in one program at 750°C.
The above parameters are designed for zirconia restorations. For glass ceramics, the recommended firing temperature is 730 °C.
Firing parameters may vary depending on the furnace type. It's recommended to test before production.
Product Information
| Manufacturer | Baot Biological Technology Co.,Ltd. |
|---|---|
| Type | With/Without Fluorescence |
| Brand | BAOT |
| Lead Time | 3~5 days for sample, 10~15 days for mass order |
| Indication | Glazing for crowns, bridges and veneers |
| Net Weight | 5g / jar |
| Solubility | ＜100 [μg/cm2] |
| Shipping Port | Support Express · Sea freight · Land freight · Air freight |
| Product Origin | Guangdong, China |
| Surface Effect | Natural gloss and smooth surface after firing |
| Bending Strength | ≥50 [MPa] |
| Application Method | Brush application before firing |
| Compatible Materials | Zirconia, PFM, PFZ and Glass Ceramic |
| Sintering Temperature | 730-950℃ |
| Transformation Temperature Tg | 495 [°C ±20] |
| Coefficient Of Thermal Expansion (25 475℃) | 9.5 [·10⁻⁶·K⁻¹ ±0.5] |