Aidite AiZir Flash

Speed Sintering Zirconia

Aizir Flash is a fast-firing zirconia material that can be sintered in 30 minutes while maintaining high aesthetics and strength. Its unique powder and production process can realize the same performance of fast-firing and slow-firing, and the translucency can reach 48% in both cases. High flexural strength meets the full range of end indications.

Parameters and application systems

• Coefficient of thermal expansion (CTE 25-500℃): (10.5±0.5)×10⁻⁶K⁻¹
• Chemical solubility: ≤100μm.cm⁻²
• Fracture toughness: ≥5MPam0.5
• Sintered density: ≥6.0g/cm³
• Vickers hardness: ≥1250HV10

Multiple sintering options

	Conventional Sintering	Rapid Sintering
Sintering time (min)	690	30
Sintering temperature (°C)	1530	1550
Light transmittance (%)	48	48
Flexural strength (MPa)	1270	1256

Product Advantage

Flexural strength 1250MPa AiZir Flash as a high-speed sintering zirconia material with flexural strength of 1250MPa

Multiple sintering options Normal sintering, fast sintering and high-speed sintering can be all achieved, even with other sintering furnaces on the market.

30 min sintering for single crowns It takes only 30 min of sintering for zirconia single crowns with no more than 3mm thickness.

Stable sintering property The same aesthetic effect are presented at high temperature and with a wide temperature range.

Digital work flow

Ai Flash materials represent Aidite's years of experience in digital processing, and we have validated the workflow of materials and equipment throughout the entire process, from the initial intraoral scan to the final restoration. The result is less labor involved, more efficient processing, better shipments, and Aidite's prompt, quality, and efficient service system.